Tin Anode Ball (Full Ball/Half Ball)
Thailand Smelting and Refining Co., Ltd.
Application
Used for normal electronic parts coating.
Alloy Composition:
| Impurities | Pure Tin Specification (%) | ||
|---|---|---|---|
| Pb 500 PPM | Pb 100 PPM | 4N Tin | |
| Tin (Sn) Min. | 99.9 | 99.9 | 99.99+ |
| Lead (Pb) Max. | 0.05 | 0.01 | 0.0030 |
| Antimony (Sb) Max. | 0.04 | 0.04 | 0.0020 |
| Silver (Ag) Max. | 0.01 | 0.01 | 0.0005 |
| Copper (Cu) Max. | 0.04 | 0.04 | 0.0020 |
| Cadmium (Cd) Max. | 0.001 | 0.001 | 0.0005 |
| Aluminium (Al) Max. | 0.001 | 0.001 | 0.0005 |
| Bismuth (Bi) Max. | 0.03 | 0.03 | 0.0010 |
| Arsenic (As) Max. | 0.03 | 0.03 | 0.0010 |
| Iron (Fe) Max. | 0.01 | 0.01 | 0.0030 |
| Zinc (Zn) Max. | 0.001 | 0.001 | 0.0005 |
Specific gravity: 7.3
Melting Temperature: 232°C
Diameter: 10, 15, 20, 22, 25 mm
Appearance: Smooth & glossy surface, without scratch, crack, dirt, and mixture of oxide.
Test method: OES, ICP
Appearance: Visual inspection
Chemical composition: Optic Emission Spectrometer, Inductively Coupled Plasma-Optical Emission Spectrometer
Size: Digimatic Micrometer
Test Report: Attached COA in every shipment.
Packing type: Plastic bag in paper box, wrapped and strapped on pallet.
Net Weight: 10 kg per box
Brand name: THAISARCO Tin Anode Ball
Marking: THAISARCO Sn 100A
Labeling on package: Lot No. Sn100A-XXX, Net WEIGHT (kg.) 10.0, No. of pieces ...............
Precautions for storage & handling: Keep in dry and clean area. Do not tear the box while moving. Open package only when product is scheduled for use.
Disclaimer:
This information is based on our experience and is, to the best of our knowledge, true and accurate. However, since the conditions for use and handling of products are beyond our control, we make no guarantee or warranty, express or implied, regarding the information, the use, handling, storage, or possession of the products, or the application of any process described herein or the results sought to be obtained. The publication hereof describing any process is not to be deemed nor taken as a license to operate under, nor recommendation to infringe any patent.